SABIC Innovative Plastics ULTEM HU2300 PEI

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	ULTEM
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics ULTEM HU2300 PEI.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.

Physical Properties	Metric	English	Comments
Specific Gravity	1.51 g/cc	1.51 g/cc	ASTM D792
Density	1.51 g/cc	0.0546 lb/inÂ³	ISO 1183
Moisture Absorption	0.500 %	0.500 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	0.90 %	0.90 %	ISO 62
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm @Thickness 3.20 mm	0.0020 - 0.0040 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	5.0 g/10 min @Load 6.60 kg, Temperature 337 Â°C	5.0 g/10 min @Load 14.6 lb, Temperature 639 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	158 MPa	22900 psi	Type I, 5 mm/min; ASTM D638
	165 MPa	23900 psi	5 mm/min; ISO 527
Tensile Strength, Yield	165 MPa	23900 psi	5 mm/min; ISO 527
	168 MPa	24400 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	2.0 %	2.0 %	5 mm/min; ISO 527
	3.0 %	3.0 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	2.0 %	2.0 %	5 mm/min; ISO 527
	3.0 %	3.0 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	9.30 GPa	1350 ksi	5 mm/min; ASTM D638
	9.50 GPa	1380 ksi	1 mm/min; ISO 527
Flexural Yield Strength	220 MPa	31900 psi	1.3 mm/min, 50 mm span; ASTM D790
	225 MPa	32600 psi	2 mm/min; ISO 178
Flexural Modulus	8.50 GPa	1230 ksi	2 mm/min; ISO 178
	9.25 GPa	1340 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	0.850 J/cm	1.59 ft-lb/in	ASTM D256
	0.900 J/cm @Temperature -30.0 Â°C	1.69 ft-lb/in @Temperature -22.0 Â°F	ASTM D256
Izod Impact, Unnotched	4.27 J/cm	8.00 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	10.0 kJ/mÂ²	4.76 ft-lb/inÂ²	80104; ISO 180/1A
	10.0 kJ/mÂ² @Temperature -30.0 Â°C	4.76 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1A
Charpy Impact, Notched	1.00 J/cmÂ²	4.76 ft-lb/inÂ²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	10.0 J @Temperature 23.0 Â°C	7.38 ft-lb @Temperature 73.4 Â°F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	16.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	8.89 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	19.8 Âµm/m-Â°C @Temperature -20.0 - 150 Â°C	11.0 Âµin/in-Â°F @Temperature -4.00 - 302 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	16.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	8.89 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	41.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	22.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	210 Â°C	410 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	210 Â°C @Thickness 6.40 mm	410 Â°F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	213 Â°C	415 Â°F	Rate B/50; ISO 306
	220 Â°C	428 Â°F	Rate B/120; ISO 306
	227 Â°C	441 Â°F	Rate B/50; ASTM D1525
Glass Transition Temp, Tg	217 Â°C	423 Â°F