SABIC Innovative Plastics ULTEM AUT210 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM AUT210 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Transparent Polyetherimide (Tg 227 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 212 degC (SABIC IP method). Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D792
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.03 %
1.03 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 11 g/10 min

@Load 6.60 kg,
Temperature 337 °C
11 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D1238
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 360 °C
16 g/10 min

@Load 11.0 lb,
Temperature 680 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 88.0 MPa
12800 psi
Type I, 5 mm/min; ASTM D638
88.0 MPa
12800 psi
5 mm/min; ISO 527
Tensile Strength, Yield 103 MPa
14900 psi
5 mm/min; ISO 527
105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 54 %
54 %
5 mm/min; ISO 527
75 %
75 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
5 mm/min; ISO 527
8.0 %
8.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.32 GPa
482 ksi
1 mm/min; ISO 527
3.59 GPa
521 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 170 MPa
24700 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.14 GPa
455 ksi
2 mm/min; ISO 178
3.33 GPa
483 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
0.380 J/cm

@Temperature -30.0 °C
0.712 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 24.4 J/cm
45.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact, Notched 1.60 J/cm²
7.61 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 33.0 J

@Temperature 23.0 °C
24.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature -40.0 - 150 °C
27.8 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature -40.0 - 150 °C
27.8 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 215 °C

@Thickness 3.20 mm
419 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 196 °C
385 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
unannealed; ASTM D648
211 °C

@Thickness 6.40 mm
412 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 221 °C
430 °F
Rate B/50; ISO 306
222 °C
432 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 227 °C
441 °F
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Descriptive Properties Value Comments
Metallized Haze Onset 212°C
SABIC Method