SABIC Innovative Plastics ULTEM 1100 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 1100 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0, V2 and 5VA listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.8 g/10 min @Load 6.60 kg, Temperature 337 °C |
8.8 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.72 GPa | 540 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 165 MPa | 23900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.72 GPa | 540 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| 15.48 J/cm @Thickness 3.20 mm |
29.00 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Gardner Impact | 23.0 J | 17.0 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 0.400 mm |
V-2 @Thickness 0.0157 in |
UL 94 |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- Radici Radilon® A RV250 (cond.) Nylon 66
- Plastcom PLASTALEN® PH 52 T 20 Polypropylene reinforced with mineral filler
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Iceberg Clay Filler
- LG Chemical SEETEC M1315 Polypropylene Impact Copolymer
- SABIC Innovative Plastics NORYL HM4025H PPE+PS (Asia Pacific)
- Hexcel® HexWeb® CR III 1/4-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Dynasol Calprene® H6140 Hydrogenated Rubber SEBS
- BASF 2- Ethylhexyl Acrylate
- Axiall 8823 Moldings & Extrusions Flexible PVC
- Nye Lubricants 799 (RL) Synthetic Oil
Copyright © lookpolymers.com All Rights Reserved