SABIC Innovative Plastics Noryl GTX GTX904 PPE+PS+PA

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl GTX GTX904 PPE+PS+PA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced; improved processing; excellent chemical resistance; 320F (160C) HDT.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D 792
Linear Mold Shrinkage, Flow 0.0090 - 0.012 cm/cm

@Thickness 3.20 mm
 0.0090 - 0.012 in/in

@Thickness 0.126 in
 SABIC Method
0.011 - 0.015 cm/cm

@Treatment Temp. 130 °C,
Time 3600 sec
 0.011 - 0.015 in/in

@Treatment Temp. 266 °F,
Time 1.00 hour
 annealed; ASTM D 955
Linear Mold Shrinkage, Transverse 0.0080 - 0.011 cm/cm

@Thickness 3.20 mm
 0.0080 - 0.011 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ASTM D 785
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 49.3 %
49.3 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 8.9 %
8.9 %
Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength 93.0 MPa
13500 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 2.27 GPa
329 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 1.49 J/cm

@Temperature -40.0 °C
 2.79 ft-lb/in

@Temperature -40.0 °F
 ASTM D 256
1.60 J/cm

@Temperature -30.0 °C
 3.00 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
2.24 J/cm

@Temperature 23.0 °C
 4.20 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 32.04 J/cm

@Temperature 23.0 °C
 60.02 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
32.04 J/cm

@Temperature -30.0 °C
 60.02 ft-lb/in

@Temperature -22.0 °F
 ASTM D 4812
32.04 J/cm

@Temperature -40.0 °C
 60.02 ft-lb/in

@Temperature -40.0 °F
 ASTM D 4812
Impact Test 31.0 J

@Temperature -40.0 °C
 22.9 ft-lb

@Temperature -40.0 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
43.0 J

@Temperature -30.0 °C
 31.7 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
46.0 J

@Temperature 23.0 °C
 33.9 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Taber Abrasion, mg/1000 Cycles 16

@Load 1.00 kg
 16

@Load 2.20 lb
 CS-17; ASTM D 1044
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C

@Thickness 6.40 mm
 320 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 125 °C

@Thickness 6.40 mm
 257 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Vicat Softening Point 238 °C
460 °F
Rate B/50; ASTM D 1525
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.49 mm
 HB

@Thickness 0.0587 in
 UL 94