SABIC Innovative Plastics Noryl FN215D PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl FN215D PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NORYL FN215 is a Noryl Engineering structural foam grade fulfilling a wide range of application requirement. Moulded with the recommended blowing agents, this material provides all the performance requirements for computer and business machine housings and cabinets.Its excellent load bearing characteristics allow for a maximum degree of integration. Its properties exceed those of many other thermoplastics and make it highly competitive with traditional materials like metal and wood. FN215 meets the requirements for flammability classification 94 V-0/5V under Underwriters' Laboratories test UL 94 Standard.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 0.880 g/cc
0.880 g/cc
ASTM D 792
Density 0.880 g/cc
0.0318 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
on tensile bar; SABIC Method
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 280 °C
10 g/10 min

@Load 4.76 lb,
Temperature 536 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
50 mm/min; ISO 527
Tensile Strength, Yield 45.0 MPa
6530 psi
50 mm/min; ISO 527
Elongation at Break 40 %
40 %
50 mm/min; ISO 527
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527
Flexural Yield Strength 60.0 MPa
8700 psi
2 mm/min; ISO 178
Flexural Modulus 2.00 GPa
290 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact Unnotched 1.60 J/cm²

@Temperature 23.0 °C
7.61 ft-lb/in²

@Temperature 73.4 °F
ISO 179/2C
Gardner Impact 25.0 - 35.0 J
18.4 - 25.8 ft-lb
SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 - 80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 - 44.4 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity 0.210 W/m-K
1.46 BTU-in/hr-ft²-°F
ISO 8302
Vicat Softening Point 105 °C
221 °F
Rate B/120; ISO 306
UL RTI, Electrical 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical without Impact 85.0 °C
185 °F
UL 746B
Flammability, UL94 V-1

@Thickness 3.00 mm
V-1

@Thickness 0.118 in
UL 94
V-0

@Thickness 6.00 mm
V-0

@Thickness 0.236 in
UL 94
5VA

@Thickness 3.90 mm
5VA

@Thickness 0.154 in
UL 94
Electrical Properties Metric English Comments
Dielectric Constant 2.2

@Frequency 1.00e+6 Hz
2.2

@Frequency 1.00e+6 Hz
IEC 60250
Dissipation Factor 0.0039

@Frequency 1.00e+6 Hz
0.0039

@Frequency 1.00e+6 Hz
IEC 60250
0.0047

@Frequency 50.0 - 60.0 Hz
0.0047

@Frequency 50.0 - 60.0 Hz
IEC 60250
Descriptive Properties Value Comments
Weight Reduction, % 23
SABIC Method