SABIC Innovative Plastics NORYL WCD883 PPE-TPE (Asia Pacific)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCD883 PPE-TPE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as jacket of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 50265-2-1 requirement. 88 Shore A hardness. Processing typically conducted on standard extrusion equipment. Wire tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 88 | 88 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 50 mm/min; ISO 527 |
| 13.0 MPa | 1890 psi | Type I, 50 mm/min; ASTM D638 | |
| 18.0 MPa | 2610 psi | UL 1581 | |
| 20.0 MPa | 2900 psi | after 7days @80°C; UL 1581 | |
| Elongation at Break | 200 % | 200 % | Type I, 50 mm/min; ASTM D638 |
| 200 % | 200 % | 50 mm/min; ISO 527 | |
| 226 % | 226 % | after 7days @136°C; UL 1581 | |
| 248 % | 248 % | UL 1581 | |
| Flexural Modulus | 0.0400 GPa | 5.80 ksi | 12.5 mm/min; ISO 178 |
| 0.0500 GPa | 7.25 ksi | 12.5 mm/min, 100 mm span; ASTM D790 | |
| Heat Distortion | 13 % @Load 0.250 kg, Temperature 100 °C |
13 % @Load 0.551 lb, Temperature 212 °F |
UL 1581 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Oxygen Index | 34 % | 34 % | ISO 4589 |
| Glow Wire Test | 775 °C | 1430 °F | IEC 60695-2-13 |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.20e+15 ohm-cm | 5.20e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 23.7 kV/mm @Thickness 2.00 mm |
602 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Smoke Density on 0.5mm plaque, Flame, Ds, max | 71 | ASTM E 662 |
| Smoke Density on 0.5mm plaque, Non-flame, Ds, max | 165 | ASTM E 662 |
| Vertical Flame Test | PASSES | EN 50265-2-1 |
Users viewing this material also viewed the following:
- LATI Latigray 53/22-01 CX/70 PP Homopolymer, Impact Modified
- Spartech Polycast SAR HP 1.25 (UL 752 Level 3) Cell Cast Acrylic
- Special Metals INCONEL® 686 Nickel Superalloy (UNS N06686) Plate 0.250 in (6.4 mm)
- Plenco 1500 Polyester, Granular, Compression Molded
- A. Schulman POLYFORT™ FPP 1605 Glass Reinforced Chemically Coupled Copolymer
- ELASTO UK Dryflex® 650600 TPE, Improved Compression Set and High Temperature Resistance, 60A Hardness
- DSM Arnitel® PB582-H Polyether Ester Elastomer (European and Asian Grade)
- Carmel Olefins CAPILENE® TG 50 Polypropylene Impact Copolymer
Copyright © lookpolymers.com All Rights Reserved