| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCD841U PPE-TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame retardant performance capable of meeting UL VW-1 requirement. 80C application temperature rating as defined by UL 1581. 84 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Melt Flow | 23 g/10 min @Load 5.00 kg, Temperature 250 °C |
23 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 84 | 84 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | 50 mm/min; ISO 527 |
| 18.0 MPa | 2610 psi | Type I, 50 mm/min; ASTM D638 | |
| 18.0 MPa | 2610 psi | UL 1581 | |
| 20.0 MPa | 2900 psi | after 7days @113°C; UL 1581 | |
| Elongation at Break | 220 % | 220 % | 50 mm/min; ISO 527 |
| 238 % | 238 % | after 7days @113°C; UL 1581 | |
| 250 % | 250 % | Type I, 50 mm/min; ASTM D638 | |
| 295 % | 295 % | UL 1581 | |
| Flexural Modulus | 0.0900 GPa | 13.1 ksi | 12.5 mm/min; ISO 178 |
| 0.0900 GPa | 13.1 ksi | 12.5 mm/min, 100 mm span; ASTM D790 | |
| Heat Distortion | 19 % @Load 0.250 kg, Temperature 100 °C |
19 % @Load 0.551 lb, Temperature 212 °F |
UL 1581 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | UL temperature rating; UL 1581 |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-13 |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.20e+15 ohm-cm | 4.20e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.6 @Frequency 1.00e+6 Hz |
2.6 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.5 kV/mm @Thickness 2.00 mm |
546 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Smoke Density on 0.5mm plaque, Flame, Ds, max | 133 | ASTM E 662 |
| Smoke Density on 0.5mm plaque, Non-flame, Ds, max | 170 | ASTM E 662 |
| VW-1 | Pass | UL 1581 |
Users viewing this material also viewed the following:
- Abatron AboWeld 7801-5/AboCure 7801-5 Epoxy (discontinued **)
- Shandong Rike Chemical ACM-3A PVC Impact Modifier ACM Resin
- Saint-Gobain Chemlam® Silver 10 Wear Resistant Industrial Laminate
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Monoplex DOS Plasticizer
- Epoxy Technology EPO-TEK® OG142-112 UV Cure Optical Epoxy
- ACC QM 140 QSI Quantum Silicones 40 Durometer Condensation Cured Moldmaking Material
- Overview of materials for Linear Low Density Polyethylene (LLDPE), Injection Molded
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N990 Filler
- Polimeri Europa Europrene® 1723 Emulsion Styrene-Butadiene Rubber
Copyright © lookpolymers.com All Rights Reserved