SABIC Innovative Plastics NORYL REN501 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL REN501 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl REN501 resin is an unfilled Post Industrial Recycle (PIR) based injection moldable modified polyphenylene ether blend comprising up to 40% PIR content. Available in black only.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Melt Flow | 7.7 g/10 min @Load 5.00 kg, Temperature 280 °C |
7.7 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 2.60 GPa | 377 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ASTM D256 |
| 0.950 J/cm @Temperature -30.0 °C |
1.78 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 26.0 J/cm | 48.7 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 49.0 J @Temperature 23.0 °C |
36.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 88.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
48.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 129 °C @Thickness 6.40 mm |
264 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 118 °C @Thickness 6.40 mm |
244 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V70B Fluoroelastomer Compound
- SABIC Innovative Plastics Cycoloy® CE1810 PC+ABS (Europe-Africa-Middle East)
- LNP NORYL® EXCP0112 PPS + Polyphenylene Ether, 40% Glass / Mineral Reinforcement (discontinued **)
- Ineos ABS LUSTROPAK® 1020 ABS, Extrusion Grade (discontinued **)
- Solvay Specialty Polymers Algoflon® L206 Polytetrafluoroethylene (PTFE)
- Sharadaa Ceramics REFCAST ULCC90 Low Cement Castables
- A. Schulman POLYBATCH™ Green 3600 Concentrate Based In Polyethylene
- Fainplast Compounds HG 82 Flexible PVC, Sheathing for High Temperatures
- Atom Adhesives AA-BOND 2103 Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved