- Aclo Accutech Polypropylene Copolymer CP0436C10L1 Calcium Reinforced
Aclo Accutech Polypropylene Copolymer CP0436C10L1 Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436C10L1 Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 59 | 59 | ASTM D785 |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 405 % | 405 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.100 GPa | 159.5 ksi | ASTM D638 |
| Flexural Strength | 12.0 MPa | 1740 psi | ASTM D790 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 51.1 °C | 124 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Geloy XP4034 ASA (Europe-Africa-Middle East)
- Quadrant EPP TIVAR® 88 W/BurnGuard, Flame Retardant Lining Material (ASTM Product Data Sheet)
- Chevron Phillips Ryton® R-4 06 PPS (Polyphenylene Sulfide) (discontinued **)
- Zeus THV Tubing
- Entec Hypro™ PP-CP35/1.5C Impact Copolymer, 35 Melt Flow
- ArcelorMittal Save 30-17 Electrical Steel
- Axiall 22930 Coax & Telecom Flexible PVC
- Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F)
Copyright © lookpolymers.com All Rights Reserved