SABIC Innovative Plastics NORYL NH4030B PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL NH4030B PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NH4030B is a modified PPE-HIPS blend that presents an excellent balance of non halogenated flame retardance, lower smoke production upon burning and low specific gravity for light weight parts. Noryl NH4030B is available in custom colors and may be an excellent material candidate for applications requiring light weight parts and may be processed by injection molding or extrusion techniques.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.27 % | 0.27 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 18.3 g/10 min @Load 5.00 kg, Temperature 280 °C |
18.3 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| 42.7 g/10 min @Load 5.00 kg, Temperature 300 °C |
42.7 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 | |
| Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 280 °C |
17 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 41 g/10 min @Load 5.00 kg, Temperature 300 °C |
41 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
| 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 27.5 % | 27.5 % | Type I, 50 mm/min; ASTM D638 |
| 27.8 % | 27.8 % | ISO 527 | |
| 27.8 % | 27.8 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.2 % | 4.2 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.43 GPa | 352 ksi | 1 mm/min; ISO 527 |
| 2.45 GPa | 355 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.38 GPa | 345 ksi | 2 mm/min; ISO 178 |
| 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.00 J/cm | 3.75 ft-lb/in | ASTM D256 |
| 1.17 J/cm @Temperature -30.0 °C |
2.19 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 46.0 J @Temperature 23.0 °C |
33.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 83.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 83.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 85.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 85.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 112 °C @Thickness 6.40 mm |
234 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 127 °C | 261 °F | Rate B/50; ASTM D1525 |
| 127 °C | 261 °F | Rate B/50; ISO 306 | |
| 128 °C | 262 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Draeger Tube Toxicity, Flaming (1.52mm) | Pass | AITM 3.0005, ABD0031 |
| Draeger Tube Toxicity, Non-Flaming (1.52mm) | Pass | AITM 3.0005, ABD0031 |
| Flame Spread Index (1.52mm) | 15 | ASTM E 162 |
| NBS Smoke Density, Flaming, 20 min (3.2 mm) | 126 | ASTM E 662 |
| NBS Smoke Density, Flaming, 4 min (1.52mm) | 29 | ASTM E 662 |
| NBS Smoke Density, Flaming, 4 min (3.2 mm) | 35 | ASTM E 662 |
| NBS Smoke Density, Non-Flaming, 4 min (1.52mm) | 7 | ASTM E 662 |
| Vertical Burn a (60s, 1.52mm) passes at | 0sec | FAR 25.853 |
| Vertical Burn b (12s, 1.52mm) passes at | 4sec | FAR 25.853 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DFL32XXC PC
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 350ºF Cure Temperature
- Plenco Valite 697-A Novolac Phenolic, Granular, Compression Molded (discontinued **)
- ICO Polymers ICORENEâ„¢ 190-3561 LMDPE Rotational Molding Resin
- Teknor Apex Tekbond® TB 2001 Thermoplastic Elastomer
- A. Schulman PP 828-31 Polypropylene Black Molding Grade Impact Polypropylene
- Elmer's Products Aron Alpha® 221F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- Axiall 9175 White 10 Rigid PVC, Molding, White 10
- Gromax CCP PBT 3010-104 10% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved