SABIC Innovative Plastics Lexan® LUX1619 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® LUX1619 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan* LUX1619 Polycarbonate resin is an extrusion grade. It is UL94 HB rated. It was designed for high light reflectance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 74 % | 74 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.73 GPa | 396 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| 1.35 J/cm @Temperature -30.0 °C |
2.53 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 21.3 J/cm | 39.9 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 69.0 J @Temperature 23.0 °C |
50.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 147 °C | 297 °F | Rate B/50; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Glow Wire Test | 850 °C | 1560 °F | IEC 60695-2-13 |
| 850 °C | 1560 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 1.50 - 3.00 mm |
1760 °F @Thickness 0.0591 - 0.118 in |
IEC 60695-2-12 |
Users viewing this material also viewed the following:
- NOVA Chemicals Dylark® 238P20 High Performance Glass Filled Styrenic
- Polymer Resources TP-IM-G30 Polybutylene Terephthalate, 30% Glass Reinforced, Impact Modified
- PolyOne Nymax™ X GMF 604 40 UV Black 148 rev 4 Polyamide 6 (Nylon 6)
- Polimeri Europa Europrene Latice® 5588 Carboxylated Styrene - Butadiene Copolymer
- SABIC Innovative Plastics LNP VERTON RV007E PA 66 (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene
- Ensinger Tecamid® 6/12 Nylon (PA612)
- Cotronics Duralco™ 126 450°F (230°C) Silver Filled Epoxy
- PolyOne Elastamax XL-0257-2 TPU-Based Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved