LyondellBasell Hifaxâ„¢ CA287AHF Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CA287AHF Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifax â„¢ CA287AHF is a thermoplastic polyolefin elastomer suitable for automotive exterior partsFeatures: Good StiffnessGood ProcessabilityGood Impact ResistanceGood Colorability PaintableMedium FlowDurableInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.890 g/cc | 0.0322 lb/in³ | ISO 1183 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | ISO 868 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527-1, -2 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527-1, -2 |
| Elongation at Break | 500 % | 500 % | ISO 527-1, -2 |
| Elongation at Yield | 13 % | 13 % | ISO 527-1, -2 |
| Flexural Modulus | 0.820 GPa | 119 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -40.0 °C |
3.81 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 51.0 kJ/m² @Temperature 10.0 °C |
24.3 ft-lb/in² @Temperature 50.0 °F |
ISO 180 | |
| 52.0 kJ/m² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop, Total Energy | 23.0 J @Temperature -30.0 °C |
17.0 ft-lb @Temperature -22.0 °F |
Instrumented; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature -30.0 - 100 °C |
55.6 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 1.2 % | 1.2 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 1.60 % @Temperature 121 °C, Time 3600 sec |
1.60 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Total Finaclear® MBF Clear Impact Polystyrene (discontinued **)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 70A, Non-Black Sulfur Cure
- Kennametal Stellite Denertiaâ„¢ N8 Nickel Dental Alloy
- Kolon KOCETAL® GF305 G/F Reinforced Acetal Resin
- Solvay Sulfuric Acid 98% Technical Grade
- Polyram PlusTek PA323G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant
- Elmer's Products Aron Alpha® 403T Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- Arkema Group Orgalloy® LE 60 HM Polyamide Alloy
- PolyOne Edgetek® PF-10GF/000 Polysulfone, Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved