Material Notes:

Structural foam: 10% weight reduction at 0.250" wall with non-brominated and non-chlorinated FR systems. Impact modified PC with excellent low-temperature impact and UV-stability.This data was supplied by SABIC-IP for the Americas region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.07 g/cc	1.07 g/cc	foam molded; ASTM D 792
	1.19 g/cc	1.19 g/cc	ASTM D 792
Linear Mold Shrinkage, Flow	0.0040 - 0.0080 cm/cm @Thickness 6.40 mm	0.0040 - 0.0080 in/in @Thickness 0.252 in	SABIC Method
Melt Flow	9.5 g/10 min @Load 1.20 kg, Temperature 300 °C	9.5 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	40.0 MPa @Thickness 6.35 mm	5800 psi @Thickness 0.250 in	ASTM D 638
Elongation at Break	3.2 % @Thickness 6.35 mm	3.2 % @Thickness 0.250 in	ASTM D 638
Tensile Modulus	2.81 GPa @Thickness 6.40 mm	408 ksi @Thickness 0.252 in	ASTM D 638
Flexural Yield Strength	72.0 MPa @Thickness 6.40 mm	10400 psi @Thickness 0.252 in	ASTM D 790
Flexural Modulus	1.89 GPa @Thickness 6.40 mm	274 ksi @Thickness 0.252 in	ASTM D 790
Izod Impact, Unnotched	9.07 J/cm @Thickness 6.40 mm, Temperature 23.0 °C	17.0 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F	ASTM D 4812
Impact Test	89.0 J @Temperature 23.0 °C	65.6 ft-lb @Temperature 73.4 °F	Instrumented Impact Total Energy; ASTM D 3763
	94.0 J @Temperature -20.0 °C	69.3 ft-lb @Temperature -4.00 °F	Instrumented Impact Total Energy; ASTM D 3763
	94.0 J @Temperature -40.0 °C	69.3 ft-lb @Temperature -40.0 °F	Instrumented Impact Total Energy; ASTM D 3763

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	131 °C @Thickness 6.40 mm	268 °F @Thickness 0.252 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	120 °C @Thickness 6.40 mm	248 °F @Thickness 0.252 in	unannealed; ASTM D 648
UL RTI, Electrical	50.0 °C	122 °F	UL 746B
UL RTI, Mechanical with Impact	50.0 °C	122 °F	UL 746B
UL RTI, Mechanical without Impact	50.0 °C	122 °F	UL 746B
Flammability, UL94	V-0 @Thickness 2.99 mm	V-0 @Thickness 0.118 in	UL 94
	5VA @Thickness 6.09 mm	5VA @Thickness 0.240 in	UL 94

Descriptive Properties	Value	Comments
FOAM - Flame Class Minimum Density, g/cm^3	1.07	-
FOAM - IMPACT 6.4 mm Wt Reduction, %	10	-
FOAM - MECHANICAL 6.4 mm Wt Reduction, %	10	-
FOAM - PHYSICAL 6.4mm Wt Reduction, %	10	-
FOAM - THERMAL 6.4mm Wt Reduction, %	10	-
UV-light, water exposure/immersion	F1	UL 746C