SABIC Innovative Plastics LNP VERTON UV00ASU PPA

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP VERTON UV00ASU PPA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* VERTON* UV00ASU is a compound based on Polyphthalamide resin containing 50% Long Glass Fiber. Added features of this material include: UV Stabilized, Heat Stabilized, Structural.
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
ISO 1183
1.67 g/cc
0.0603 lb/in³
ASTM D792
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Time 86400 sec
 0.0020 in/in

@Time 24.0 hour
 ASTM D955
0.0020 cm/cm

@Time 86400 sec
 0.0020 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0048 cm/cm

@Time 86400 sec
 0.0048 in/in

@Time 24.0 hour
 ISO 294
0.0050 cm/cm

@Time 86400 sec
 0.0050 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 222 MPa
32200 psi
ISO 527
257 MPa
37300 psi
ASTM D638
Tensile Strength, Yield 222 MPa
32200 psi
ISO 527
257 MPa
37300 psi
ASTM D638
Elongation at Break 1.4 %
1.4 %
ISO 527
1.8 %
1.8 %
ASTM D638
Elongation at Yield 1.4 %
1.4 %
ISO 527
1.8 %
1.8 %
ASTM D638
Tensile Modulus 19.22 GPa
2788 ksi
1 mm/min; ISO 527
19.3 GPa
2800 ksi
50 mm/min; ASTM D638
Flexural Strength 386 MPa
56000 psi
ASTM D790
393 MPa
57000 psi
ISO 178
Flexural Modulus 17.0 GPa
2470 ksi
ISO 178
17.23 GPa
2499 ksi
ASTM D790
Izod Impact, Notched 2.67 J/cm
5.00 ft-lb/in
ASTM D256
Izod Impact, Unnotched 12.28 J/cm
23.01 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 41.0 kJ/m²
19.5 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 78.0 kJ/m²
37.1 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 9.00 J
6.64 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 7.00 J
5.16 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 17.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
31.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 17.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 14.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 8.00 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
15.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 8.33 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 296 °C
565 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
291 °C

@Thickness 3.20 mm
 556 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 272 °C
522 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
266 °C

@Thickness 3.20 mm
 511 °F

@Thickness 0.126 in
 unannealed; ASTM D648