SABIC Innovative Plastics LNP VERTON UV00AS PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON UV00AS PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Verton* UV00AS is a compound based on Polyphthalamide resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| 1.67 g/cc | 0.0603 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0048 cm/cm @Time 86400 sec |
0.0048 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 222 MPa | 32200 psi | ISO 527 |
| 257 MPa | 37300 psi | ASTM D638 | |
| Tensile Strength, Yield | 222 MPa | 32200 psi | ISO 527 |
| 257 MPa | 37300 psi | ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D638 | |
| Elongation at Yield | 1.4 % | 1.4 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D638 | |
| Tensile Modulus | 19.22 GPa | 2788 ksi | 1 mm/min; ISO 527 |
| 19.3 GPa | 2800 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 386 MPa | 56000 psi | ASTM D790 |
| 393 MPa | 57000 psi | ISO 178 | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | ISO 178 |
| 17.23 GPa | 2499 ksi | ASTM D790 | |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.28 J/cm | 23.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 41.0 kJ/m² | 19.5 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 78.0 kJ/m² | 37.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 31.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 14.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 15.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.33 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 296 °C | 565 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 291 °C @Thickness 3.20 mm |
556 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 272 °C | 522 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 266 °C @Thickness 3.20 mm |
511 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-60-15 Cellular Urethane Foam
- Abatron 440 GRA5 A/B Filled Potting Compound (discontinued **)
- NIZHNEKAMSKNEFTEKHIM PE 4252A (524H1) High Density Polyethylene
- SABIC Innovative Plastics Valox® IQ507 PBT+PC
- Borealis BorPEX™ HE1878E High Density Polyethylene Powder for Crosslinked Pipes
- Eurostar Star L PA D51 PA6, Injection Molded
- Engineered Plastics EPPC 1514B Polycarbonate
- BASF Ultramid® A4H BK 00464 PA66 (Dry)
- Dow Corning EG-6301
Copyright © lookpolymers.com All Rights Reserved