SABIC Innovative Plastics LNP VERTON RX970079 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RX970079 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* RX970079 is a compound based on PA 66 resin containing Long Glass Fiber and PTFE. Added features include; Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % @Time 86400 sec |
0.90 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0023 cm/cm @Time 86400 sec |
0.0023 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0083 cm/cm @Time 86400 sec |
0.0083 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 188 MPa | 27300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.2 GPa | 1480 ksi | 1 mm/min; ISO 527 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 15.0 J | 11.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
14.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
31.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 264 °C | 507 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- KaMin Polyfil® XB Kaolin Clay - Waterwashed
- Karina E 500D08/201 Beige PVC Compound
- Techmer ES Plastiblend® PA6/6,6 IM 5050 BK MB Nylon 6/66
- Styron XZ 97222.00 SB Latex
- Sax Polymers SAXALEN PPH335T20 Polypropylene Homopolymer, 20% Talc Filled
- Wall Colmonoy COLMONOY® 6 Nickel-Base Hard-Surfacing Alloy With Chromium Boride
- Fainplast Compounds AP 86 Flexible PVC, Flame Retardant Insulation
- DuPont Performance Polymers Zytel® 103FHS BKB009 Nylon 66 (Unverified Data**)
- Asahi Kasei Xyron® A0501 PPE/PA
- Schott Glass 8241 Alkaline Earth Aluminosilicate Glass
Copyright © lookpolymers.com All Rights Reserved