Techmer ES HiFillÂ® PA6/6 GF10 TL10 BK 10% Glass Filled

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled , Nylon 66, Heat Stabilized , Nylon 66, PTFE Filled
Manufacturer	Techmer ES
Trade Name	HiFill®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES HiFillÂ® PA6/6 GF10 TL10 BK 10% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by Weight Additive: Heat Stabilizer and PTFE Lubricant(10%)Features: Lubricated and Heat StabilizedAppearance: BlackInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.33 g/cc	0.0480 lb/inÂ³	ASTM D792
Water Absorption	0.75 % @Time 86400 sec	0.75 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Thickness 3.17 mm	0.0070 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	117	117	ASTM D785
Tensile Strength, Yield	79.3 MPa	11500 psi	ASTM D638
Elongation at Break	3.5 %	3.5 %	ASTM D638
Flexural Strength	117 MPa	17000 psi	ASTM D790
Flexural Modulus	3.72 GPa	540 ksi	ASTM D790
Izod Impact, Notched	0.534 J/cm @Thickness 3.17 mm	1.00 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	54.0 Âµm/m-Â°C	30.0 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	232 Â°C	450 Â°F	Unannealed; ASTM D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.00e+14 ohm-cm	3.00e+14 ohm-cm	ASTM D257
Dielectric Strength	19.3 kV/mm	490 kV/in	Method A (Short-Time); ASTM D149