Ineos R01C-01 Polypropylene Random Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Blow Molding Grade , Polypropylene, Impact Modified; Molded/Extruded , Polypropylene, Sheet/Thermoforming Grade |
| Manufacturer | Ineos Olefins & Polymers USA |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos R01C-01 Polypropylene Random Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a low flow rate, high clarity random copolymer designed for extrusion, thermoforming and blow molding. Applications that require good see-through clarity combined with good heat resistance and refrigerator temperature impact properties can benefit from its use. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsThermoformed packaging (cups, containers, lidding)Extrusion blow molded containers and bottlesExtruded sheet and profilesBenefitsExcellent clarityExcellent processabilityGood impact resistance at room and refrigerator temperaturesInformation provided by Ineos Olefins & Polymers USA
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.9 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 84 | 84 | ASTM D785 |
| Tensile Strength, Yield | 27.9 MPa @Temperature 23.0 °C |
4040 psi @Temperature 73.4 °F |
ASTM D638 |
| Elongation at Yield | 13.8 % | 13.8 % | ASTM D638 |
| Flexural Modulus | 0.896 GPa @Temperature 23.0 °C |
130 ksi @Temperature 73.4 °F |
test speed 0.05'/min; ASTM D790 |
| 1.18 GPa @Temperature 23.0 °C |
171 ksi @Temperature 73.4 °F |
test speed 0.5'/min; ASTM D790 | |
| Izod Impact, Notched | 2.99 J/cm @Temperature 4.00 °C |
5.60 ft-lb/in @Temperature 39.2 °F |
1/8'' notched bar, partial failure, (refrigerator temperature); ASTM D256 |
| 5.13 J/cm @Temperature 23.0 °C |
9.60 ft-lb/in @Temperature 73.4 °F |
1/8'' notched bar, partial failure, (Room temperature); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 76.1 °C | 169 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 14.4 % @Temperature 23.0 °C |
14.4 % @Temperature 73.4 °F |
50-mil plaque, % Transmittance; ASTM D1003 |
| Gloss | 94.8 % | 94.8 % | 60° angle; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Process | Blow Molding | |
| Extrusion | ||
| Thermoforming | ||
| Region | Mexico | Bamberger Polymers Distribution |
| US & Canada | Bamberger Polymers Distribution |
Users viewing this material also viewed the following:
- Quadrant EPP Cestilene™ HD 1000 R Polyethylene
- Solvay Specialty Polymers Galden® SV55 PFPE Solvent
- Toho Tenax Besfight® G30-500 3K HTA-7C EP01 Continuous Filament Carbon Fiber
- American Elements Magnesium Nanoparticles
- Tra-Con Tra-Bond F120 Fast Cure Epoxy Adhesive
- Covestro Makrolon® 6555 Polycarbonate, Injection Grade
- Eurotec® Tecodur® PB7 GR15 NL RT PBT, 15% glass fiber reinforced, PTFE modified, natural
- Denka REOMER G G3015 Thermoplastic Elastomer, For Extrusion
- Bhansali Engineering Abstron KU602L ABS Heat Resistant
- Overview of materials for Polypropylene with 30% Calcium Carbonate (CaCO3) Filler
Copyright © lookpolymers.com All Rights Reserved