SABIC Innovative Plastics LNP VERTON MX02795 PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON MX02795 PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Verton* MX02795 is a compound based on Polypropylene resin containing Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0027 cm/cm @Time 86400 sec |
0.0027 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0053 cm/cm @Time 86400 sec |
0.0053 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
| Tensile Strength, Yield | 111 MPa | 16100 psi | ISO 527 |
| 117 MPa | 17000 psi | ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Elongation at Yield | 2.1 % | 2.1 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Tensile Modulus | 8.96 GPa | 1300 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 158 MPa | 22900 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT SF-40LGF/001 Natural Polyphenylene Sulfide (PPS)
- SABIC Innovative Plastics Lexan® FXD1414T PC Copolymer
- Mearthane Durethaneâ„¢ C Foams DCF and DCM Polyurethane
- Michelman® Michem® Coat 40Y Water resistant, cold set and hot melt gluable coating
- Chase Plastics CP Pryme® NN143GL (COND, 50% RH) Nylon 66, 43% Glass Fiber Reinforced, Internally Lubricated
- Polyplastics FR-PET® CN9015 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose
- ELASTO UK Dryflex® 602300S SEBS Based Material, Filled Qualities, 30A Hardness, Black
- CP-Polymer-Technik Wellamid® 6600 HWUVCP Nylon 66, UV Stabilized, Heat Stabilized, Dry
- DuPont Teijin Films Mylar® LJP Polyester Film, 500 Gauge
- 3M 12038 Black 3/8" (9.5 mm) Polyurethane Foam
Copyright © lookpolymers.com All Rights Reserved