SABIC Innovative Plastics LNP Thermocomp WB006 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Bead Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp WB006 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* WB006 is a compound based on Polybutylene Terephalate resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D 792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.060 % | 0.060 % | 23°C / 50% RH; ISO 62 |
| 0.050 % @Time 86400 sec |
0.050 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D 638 |
| 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.4 % | 4.4 % | 5 mm/min; ISO 527 |
| 5.6 % | 5.6 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 3.7 % | 3.7 % | 5 mm/min; ISO 527 |
| 4.2 % | 4.2 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 4.07 GPa | 590 ksi | 50 mm/min; ASTM D 638 |
| 4.20 GPa | 609 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 3.60 GPa | 522 ksi | 2 mm/min; ISO 178 |
| 3.98 GPa | 577 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.220 J/cm @Temperature 23.0 °C |
0.412 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 1.72 J/cm @Temperature 23.0 °C |
3.22 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 71.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
39.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 186 °C @Thickness 3.20 mm |
367 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Murtfeldt Original Material ”S”® plus + LF ESD Polyethylene, Low Friction Conductive
- PTS Trimid® N66-SG33-BK 33% Glass Reinforced, High Impact Black Nylon 6/6
- Lord Adhesives 5 Mix-In Accelerator for 200, 400, 500 Series
- SABIC Innovative Plastics Ultem 1010RV PEI (Asia Pacific)
- SK Chemicals SKYTHANE® 310 Hotmelt Grade UB Polyurethane
- ExxonMobil Gargoyle Arctic 230 SHC 200 Series
- Dow LDPE 493A Low Density Polyethylene, Film Grade
- Asahi Kasei Thermofil P-40TC-1156 40% Talc Reinforced, Heat Stabilized
- Austin Novel Materials Texalan® 395A Polyester-based TPU
- CENTROPLAST CENTROLEN PP-H Polypropylene homopolymer
Copyright © lookpolymers.com All Rights Reserved