SABIC Innovative Plastics LNP LUBRICOMP RFL36U PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFL36U PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFL36U is a compound based on Nylon 66 resin containing 15% PTFE, 30% Glass Fiber. Added features of this grade include: Wear Resistant, UV Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.370 % | 0.370 % | 50% RH, 24 hrs; ASTM D570 |
| 0.580 % | 0.580 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 158 MPa | 22900 psi | 5 mm/min; ISO 527 |
| 160 MPa | 23200 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 160 MPa | 23200 psi | Type I, 5 mm/min; ASTM D638 |
| 168 MPa | 24400 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 |
| 2.8 % | 2.8 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 |
| 2.8 % | 2.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.44 GPa | 1514 ksi | 1 mm/min; ISO 527 |
| 11.66 GPa | 1691 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 219 MPa | 31800 psi | ISO 178 |
| 233 MPa | 33800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 233 MPa | 33800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.89 GPa | 1290 ksi | 2 mm/min; ISO 178 |
| 9.26 GPa | 1340 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.80 J/cm | 16.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 54.0 kJ/m² | 25.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.67 | 0.67 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.61 | 0.61 | ASTM D3702 Modified |
| K (wear) Factor | 10.1 x 10-8 mm³/N-M | 5.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 78.5 µm/m-°C @Temperature -30.0 - 30.0 °C |
43.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 244 °C | 471 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 249 °C @Thickness 3.20 mm |
480 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPH4504HEU PPC (Europe-Africa-Middle East)
- Overview of materials for Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
- Gromax BFG30-FH00B2 Nylon 6 30% Glass Filled (Dry)
- Sibur 153-10K 1st Grade Polyethylene for Cable Production
- Borealis Daplen™ ED117AE Polypropylene TPO Compound
- Chase Plastics CP Pryme® N300L (DAM) Nylon 6 (Utility Grade), Internally Lubricant
- Chase Plastics CP Pryme® NN230GL (COND, 50% RH) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated
- Zeon Chemicals Nipol® 1032-45 Nitrile Elastomer
- DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 50 Gauge
- ExxonMobil Santoprene® 8291-60B500 Thermoplastic Vulcanizate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved