SABIC Innovative Plastics LNP Thermocomp SF00A PA12 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp SF00A PA12 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass filled Nylon 12This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D 792 |
| 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 113 MPa | 16400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 113 MPa | 16400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 12.28 GPa | 1781 ksi | 1 mm/min; ISO 527 |
| 12.8 GPa | 1860 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 143 MPa | 20700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 148 MPa | 21500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 0.0100 GPa | 1.45 ksi | 2 mm/min; ISO 178 |
| 8.93 GPa | 1300 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.970 J/cm @Temperature 23.0 °C |
1.82 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.77 J/cm @Temperature 23.0 °C |
10.8 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 1.00 kJ/m² @Temperature 23.0 °C |
0.476 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 16.0 J | 11.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 176 °C @Thickness 3.20 mm |
349 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 176 °C | 349 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 166 °C @Thickness 3.20 mm |
331 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- MV Labs LI890 LiOH.H2O Lithium hydroxide monohydrate
- Niche Polymer PPCM15BK Copolymer PP
- 3M Dyneon™ Fluorel™ FC-2261Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Advanced Elastomer Systems Santoprene® 8281-55 Thermoplastic Rubber (discontinued **)
- PolyOne Lubri-Tech™ PS-30GF/10T Polybutylene Terephthalate (PBT), Glass Filled, PTFE Lubricated (discontinued
- Arlon A3020-B004-12 Silicone Rubber/Fiberglass Laminate (discontinued **)
- 3M 7042 Screen Printable Polyester Performance LabelProducts
- BASF Diisopropanolamine S
- BASF Hydroxypivalic Acid Neopentylglycolester Molten (HPN)
- Lehmann & Voss LUVOCOM® 1105-8135/OR PEEK, unreinforced, easy flowing
Copyright © lookpolymers.com All Rights Reserved