SABIC Innovative Plastics LNP Thermocomp RF005 PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RF005 PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RF005 is a compound based on Nylon 66 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Time 86400 sec |
0.014 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 132 MPa | 19100 psi | ASTM D 638 |
| 139 MPa | 20200 psi | ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D 638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 8.30 GPa | 1200 ksi | 1 mm/min; ISO 527 |
| 9.10 GPa | 1320 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D 790 |
| 205 MPa | 29700 psi | ISO 178 | |
| Flexural Modulus | 7.23 GPa | 1050 ksi | ASTM D 790 |
| 8.30 GPa | 1200 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm @Temperature 23.0 °C |
1.29 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.80 J/cm @Temperature 23.0 °C |
8.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² @Temperature 23.0 °C |
15.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C @Thickness 3.20 mm |
496 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 245 °C @Thickness 3.20 mm |
473 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPHC K2040H Polypropylene, Mineral Reinforced
- DuPont™ Surlyn® 8670 Ionomer Resin, Sodium (discontinued **)
- Momentive Performance Materials AC-6028 Boron Nitride (BN) Powder
- Ineos ABS Lustran® Ultra 4000 PG ABS Pellets (a-methylstyrene-SAN-modified), Electroplating Grade
- Solvay MACKADET® EQ-178 Surfactant
- DSM Akulon® S223-G4U (Cond.) 23% Glass Reinforced Nylon 66 (North America)
- ConocoPhillips Conoflex® 32 SRI Lubricant ISO
- ConocoPhillips 32 Spectrum Cutting Oil
- Trelleborg Emerson & Cuming Stycast® 4640-25 Two-Component Silicone Flexible Encapsulant
- A. Schulman POLYFORT™ FPP 1609 Mica Fortified Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved