SABIC Innovative Plastics LNP Thermocomp OF004AER PPS
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp OF004AER PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D 792 |
| 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0041 cm/cm @Time 86400 sec |
0.0041 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527 |
| 93.0 MPa | 13500 psi | ASTM D 638 | |
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO 527 |
| 93.0 MPa | 13500 psi | ASTM D 638 | |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527 |
| 1.1 % | 1.1 % | ASTM D 638 | |
| Elongation at Yield | 0.90 % | 0.90 % | ISO 527 |
| 1.1 % | 1.1 % | ASTM D 638 | |
| Tensile Modulus | 9.58 GPa | 1390 ksi | 50 mm/min; ASTM D 638 |
| 9.86 GPa | 1430 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D 790 |
| 117 MPa | 17000 psi | ISO 178 | |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D 790 |
| 9.00 GPa | 1310 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.56 J/cm @Temperature 23.0 °C |
4.80 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 28.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 29.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 227 °C | 441 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 277 °C @Thickness 3.20 mm |
531 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 263 °C | 505 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylac® EX28 ABS
- SABIC Innovative Plastics Lexan® SLX2271T PC Copolymer
- Michelman® Michem® Glide 37 Nonionic PTFE dispersion
- H.C. Starck Grade A Zirconium Diboride, ZrB2
- SABIC Innovative Plastics LNP LUBRICOMP UCL36S PPA (Asia Pacific)
- Unitika TERRAMAC TE-7000 Polylactic Acid (PLA)
- Arkema Group VOLTALEF® 300 HD PCTFE
- Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal
Copyright © lookpolymers.com All Rights Reserved