PolyOne Edgetek® XT XT-100-BU01-HF Polycarbonate + PBT (PC+PBT)

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer	PolyOne Corporation
Trade Name	Edgetek®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Edgetek® XT XT-100-BU01-HF Polycarbonate + PBT (PC+PBT).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

EDGETEK™ XT High Performance Polymers are polycarbonate and polyester alloys that combine strength, durability and chemical resistance. The Edgetek XT product family includes a complete line of general purpose, UV stable and low-temperature impact grades for use in a wide range of demanding applications and severe operating environments plus customized formulations to meet specialized requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.21 g/cc	1.21 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm	0.0070 - 0.0090 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	60.7 MPa	8800 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	110 %	110 %	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	89.6 MPa	13000 psi	ASTM D790
Flexural Modulus	2.34 GPa	339 ksi	ASTM D790
Izod Impact, Notched	1.30 J/cm @Thickness 1.57 mm, Temperature -20.0 °C	2.44 ft-lb/in @Thickness 0.0618 in, Temperature -4.00 °F	Injection Molded; ASTM D256A
	8.00 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	15.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	98.3 °C @Thickness 6.35 mm	209 °F @Thickness 0.250 in	Unannealed; ASTM D648

Processing Properties	Metric	English
Melt Temperature	260 - 277 °C	500 - 531 °F
Mold Temperature	65.6 - 87.8 °C	150 - 190 °F
Drying Temperature	110 °C	230 °F
Dry Time	2.00 hour	2.00 hour

Descriptive Properties	Value	Comments
Additive	UV Stabilizer
Features	High Flow
Forms	Pellets
Generic Material	PC+PBT
Generic Name	Polycarbonate + PBT (PC+PBT)
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America