SABIC Innovative Plastics LNP Thermocomp OF002A PPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp OF002A PPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| 1.42 g/cc | 0.0513 lb/in³ | ASTM D 792 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D 638 |
| 49.0 MPa | 7110 psi | ISO 527 | |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D 638 |
| 49.0 MPa | 7110 psi | ISO 527 | |
| Elongation at Break | 0.60 % | 0.60 % | ASTM D 638 |
| 0.60 % | 0.60 % | ISO 527 | |
| Elongation at Yield | 0.60 % | 0.60 % | ASTM D 638 |
| 0.60 % | 0.60 % | ISO 527 | |
| Tensile Modulus | 7.15 GPa | 1040 ksi | 1 mm/min; ISO 527 |
| 8.96 GPa | 1300 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 82.0 MPa | 11900 psi | ASTM D 790 |
| 98.0 MPa | 14200 psi | ISO 178 | |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D 790 |
| 6.40 GPa | 928 ksi | ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C |
0.599 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 0.900 J/cm @Temperature 23.0 °C |
1.69 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 272 °C | 522 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 271 °C @Thickness 3.20 mm |
520 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID® 6/66 GF 15 GB 15 PA6/66 reinforced with glass fiber, glass beads
- PSM Industries Pacific Sintered Metals Steel F-240-S(HT) Powdered Metal
- ExxonMobil HD 6605.29 Injection Molding Resin (discontinued **)
- Huntsman HY 283 Cycloaliphatic Amine
- Isoflon PC Polycarbonate
- Cosmic Plastics K77 Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- Axiall 16860 Wire & Cable Flexible PVC
- Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/4hr/AC
- Arkema Group Oroglas® V 825 HID Acrylic, UV, Heat Resistant (discontinued **)