SABIC Innovative Plastics LNP Thermocomp IF006S PA 6/12 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 612
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp IF006S PA 6/12 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
LNP* Thermocomp* IF006S is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
1.32 g/cc
0.0477 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0011 - 0.0016 cm/cm

@Time 86400 sec
 0.0011 - 0.0016 in/in

@Time 24.0 hour
 ISO 294
0.0010 - 0.0020 cm/cm

@Time 86400 sec
 0.0010 - 0.0020 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0066 - 0.0071 cm/cm

@Time 86400 sec
 0.0066 - 0.0071 in/in

@Time 24.0 hour
 ISO 294
0.0070 - 0.0080 cm/cm

@Time 86400 sec
 0.0070 - 0.0080 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 178 MPa
25800 psi
ISO 527
182 MPa
26400 psi
ASTM D 638
Elongation at Break 3.4 %
3.4 %
ISO 527
3.7 %
3.7 %
ASTM D 638
Tensile Modulus 9.58 GPa
1390 ksi
50 mm/min; ASTM D 638
10.32 GPa
1497 ksi
1 mm/min; ISO 527
Flexural Strength 250 MPa
36300 psi
ISO 178
289 MPa
41900 psi
ASTM D 790
Flexural Modulus 8.83 GPa
1280 ksi
ISO 178
9.30 GPa
1350 ksi
ASTM D 790
Izod Impact, Notched 1.38 J/cm

@Temperature 23.0 °C
 2.59 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 12.28 J/cm

@Temperature 23.0 °C
 23.01 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 14.0 kJ/m²

@Temperature 23.0 °C
 6.66 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 78.0 kJ/m²

@Temperature 23.0 °C
 37.1 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
14.0 J

@Temperature 23.0 °C
 10.3 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
 22.5 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
41.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 73.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
73.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 213 °C

@Thickness 3.20 mm
 415 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 198 °C

@Thickness 3.20 mm
 388 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL 94 by SABIC-IP