SABIC Innovative Plastics LNP Thermocomp 2Z004 FP-E (EFTE)
| Category | Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE , Fluorocarbon ETFE, with Glass or Carbon Fiber Filler |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp 2Z004 FP-E (EFTE).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* 2Z004 is a compound based on Ethylenetetrafluoroethylene (ETFE) containing Milled Glass.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | ASTM D 792 |
| Density | 1.83 g/cc | 0.0661 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.00 % @Time 86400 sec |
0.00 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D 638 |
| 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 5 mm/min; ISO 527 |
| 29.0 MPa | 4210 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 53 % | 53 % | Type I, 5 mm/min; ASTM D 638 |
| 78 % | 78 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 22 % | 22 % | 5 mm/min; ISO 527 |
| 23 % | 23 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 1.51 GPa | 219 ksi | 1 mm/min; ISO 527 |
| 1.70 GPa | 247 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 24.0 MPa | 3480 psi | ISO 178 |
| Flexural Modulus | 1.21 GPa | 175 ksi | 2 mm/min; ISO 178 |
| 1.28 GPa | 186 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 6.15 J/cm @Temperature 23.0 °C |
11.5 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 13.4 J/cm @Temperature 23.0 °C |
25.1 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 37.0 kJ/m² @Temperature 23.0 °C |
17.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 119 kJ/m² @Temperature 23.0 °C |
56.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 26.0 J @Temperature 23.0 °C |
19.2 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
48.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 7445L (EPC57MA) Propylene and Ethylene Block Polymer
- Resinlab® AR 4315 Metal Bonding Methacrylate Adhesive
- LATI Laril 13-V1KC PPOm, Mineral Reinforced, Flame Retardant
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 45-LR-9 TPE
- Styron Magnumâ„¢ 9085 ABS
- A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT
- Adell BH-38 Nylon 6, 40% Mineral Filled
- ATI Allvac® Nickelvac® 23 UNS N08020 Specialty Steel
- Gwent Electronic Materials C2010809D3 Silver Ink
Copyright © lookpolymers.com All Rights Reserved