SABIC Innovative Plastics LNP THERMOCOMP ZF0089 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP ZF0089 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* ZF0089 is a compound based on PPE+PS resin containing 40% Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0700 % | 0.0700 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0900 % | 0.0900 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 8.00 MPa | 1160 psi | 5 mm/min; ISO 527 |
| 101 MPa | 14600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.80 % | 0.80 % | 5 mm/min; ISO 527 |
| 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.28 GPa | 1781 ksi | 1 mm/min; ISO 527 |
| 13.02 GPa | 1888 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 131 MPa | 19000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.8 GPa | 1710 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 11.94 GPa | 1732 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.32 J/cm | 6.22 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 53.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ 1200 A HS Natural A Polyamide 66 (Nylon 66)
- Total Finathene® SR 572 HDPE blow molding (discontinued **)
- LyondellBasell Montell 12C01G2 Clarity LLDPE
- LG Chemical LUCEL N109LDS POM, Chemical Resistance
- Minelco UltraCarb LH15X Hydrated Magnesium Calcium Carbonate
- Stir SpA IN 3080 (PVC)
- Covestro Makrolon® 2405 Polycarbonate, Injection Grade
- Alliance Polymers Viprene™ G85A-32U-BLK Thermoplastic Vulcanizate Elastomer
- Ineos Nova 207 Crystal Polystyrene High Heat, High Flow Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved