- Polyethersulfone (PES), 10%Glass Fiber Filled
- Techmer ES HiFill® PES GF10 10% Glass Filled
Techmer ES HiFill® PES GF10 10% Glass Filled
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 10%Glass Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PES GF10 10% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.18 % @Time 86400 sec |
0.18 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.17 mm |
0.0010 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm |
1.40 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.4 µm/m-°C | 28.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Hong Kun Group 4-Fluoro-3-methylacetophenone Pharmaceutical Intermediate
- SABIC Innovative Plastics LNP LUBRICOMP RFL26 PA 66
- SABIC Innovative Plastics LNP THERMOCOMP KF004AL Acetal Homopoly (Asia Pacific)
- Eastman Tritan MX710 Copolyester
- ExxonMobil Univis N 32
- Alliance BIF-11 Bonded (Composite) Magnetic Material
- 3M Scotchcal™ ElectroCut™ 7725-130 Graphic Film
- Fainplast Compounds MPH 75/T Medical Flexible PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved