Kingfa PET-RG30 Flame Retardant, 30% Glass Fiber Reinforced PET

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant
Manufacturer	Kingfa Sci. & Tech. Co.
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Kingfa PET-RG30 Flame Retardant, 30% Glass Fiber Reinforced PET.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features:Flame retardantHigh strengthGood heat resistanceOutstanding electrical propertiesApplications:Injection moldingConnectorsRelayBobbinsSocketsE & E partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.65 g/cc @Temperature 23.0 Â°C	1.65 g/cc @Temperature 73.4 Â°F	ASTM D792
Water Absorption	0.070 % @Temperature 23.0 Â°C, Time 86400 sec	0.070 % @Temperature 73.4 Â°F, Time 24.0 hour	ASTM D570
Linear Mold Shrinkage	0.0030 - 0.0090 cm/cm @Temperature 23.0 Â°C	0.0030 - 0.0090 in/in @Temperature 73.4 Â°F	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength at Break	140 MPa	20300 psi	10mm/min; ASTM D638
Elongation at Break	2.3 %	2.3 %	10mm/min; ASTM D638
Flexural Strength	210 MPa	30500 psi	2mm/min; ASTM D790
Flexural Modulus	10.5 GPa	1520 ksi	2mm/min; ASTM D790
Izod Impact, Notched	0.800 J/cm @Thickness 3.20 mm, Temperature 23.0 Â°C	1.50 ft-lb/in @Thickness 0.126 in, Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	240 Â°C @Thickness 6.40 mm	464 Â°F @Thickness 0.252 in	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	225 Â°C @Thickness 6.40 mm	437 Â°F @Thickness 0.252 in	ASTM D648
Flammability, UL94	V-0 @Thickness 0.750 mm	V-0 @Thickness 0.0295 in
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257

Processing Properties	Metric	English	Comments
Processing Temperature	<= 270 Â°C	<= 518 Â°F
Rear Barrel Temperature	235 - 255 Â°C	455 - 491 Â°F	Start Point: 245Â°C
Middle Barrel Temperature	245 - 265 Â°C	473 - 509 Â°F	Start Point: 250Â°C
Front Barrel Temperature	255 - 275 Â°C	491 - 527 Â°F	Start Point: 260Â°C
Melt Temperature	255 - 275 Â°C	491 - 527 Â°F	Start Point: 260Â°C
Mold Temperature	80.0 - 120 Â°C	176 - 248 Â°F	Start Point: 100Â°C
Drying Temperature	120 - 140 Â°C @Time 10800 - 18000 sec	248 - 284 Â°F @Time 3.00 - 5.00 hour	Pre-dry

Descriptive Properties	Value	Comments
Glass Fiber Content (%)	30
Injection Speed	Moderate to High