SABIC Innovative Plastics LNP THERMOCOMP WX05456 Polyester, TP
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WX05456 Polyester, TP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* WX05456 is a compound based on Polyester, TP resin containing Mineral.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| 1.546 g/cc | 0.05585 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0147 cm/cm @Time 86400 sec |
0.0147 in/in @Time 24.0 hour |
ISO 294 |
| 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0151 cm/cm @Time 86400 sec |
0.0151 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 |
| 48.0 MPa | 6960 psi | ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D638 | |
| Tensile Modulus | 4.22 GPa | 612 ksi | 50 mm/min; ASTM D638 |
| 4.65 GPa | 674 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 88.0 MPa | 12800 psi | ISO 178 |
| 90.0 MPa | 13100 psi | ASTM D790 | |
| Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
| 4.39 GPa | 637 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.97 J/cm | 3.69 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 58.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 58.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 66.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 66.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 171 °C @Thickness 3.20 mm |
340 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 71.0 °C @Thickness 3.20 mm |
160 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JAX21P Polyvinyl Chloride, Flexible (PVC, Flexible)
- Ritelok GM18 Aluminum Parts Gasket Maker
- Karina 65/213 Clear PVC Compound
- Solvay Specialty Polymers FOMBLIN® Y04 PFPE Lubricant
- Tisan TISARBON® Flame Retardant (V0) Polycarbonate
- Hexcel® HexForce™ KA060 Aramid and High Performance Fabrics
- ExxonMobil LDPE LD 129.24 Low Density Polyethylene Resin
- Dura-Bar 120-90-02 Continuously Cast Ductile Iron Bar Stock ASTM A536
- Dynasol Calprene® 401 Thermoplastic Rubber SBS Dry
- SABIC Innovative Plastics LNP THERMOCOMP GX94043L PSU (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved