Styrolution PS 147F GPPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Transparent Grade |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution PS 147F GPPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolution PS 147F is a highly transparent GPPS grade. It gives excellent mechanical and heat resistance properties while providing with easy processability and short cycle time.Medium FlowEasy processabilityGood mechanical and heat resistance propertiesInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.046 g/cc | 0.03779 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ISO 294-4 |
| Melt Flow | 6.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 150 MPa | 21800 psi | ISO 2039-1 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527 |
| Flexural Strength | 98.0 MPa | 14200 psi | ISO 178 |
| Charpy Impact Unnotched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 |
| Vicat Softening Point | 95.0 °C @Load 5.10 kg |
203 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 100 °C @Load 1.02 kg |
212 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
IEC 60250 |
| 2.5 @Frequency 1.00e+6 Hz |
2.5 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 135 kV/mm @Thickness 1.50 mm |
3430 kV/in @Thickness 0.0591 in |
Short Time; IEC 60243-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | ISO 294 |
| Mold Temperature | 10.0 - 60.0 °C | 50.0 - 140 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
Users viewing this material also viewed the following:
- PPT FP150 Fully Sintered Ferrite Powder
- GEHR Plastics PET Polyethylene Terephthalate
- Latrobe Tatmo-Vâ„¢ AISI M7 High Speed Steel
- SGL Carbon Group SIGRAFIL C® C10 S003 GLY Staple Carbon Fiber, Glycerine Sizing
- DuPont Teijin Films Teijin® Tetoron® OLF Polyester Film, 700 Gauge
- Axiall Tuf-Stif 2804 Rigid PVC, Extrusion
- BASF Elastollan® 1180A Polyether Type Polyurethane Elastomer
- DuPont Elvax® 4355 Ethylene Vinyl Acetate (discontinued **)
- Dielectric Polymers NT-701 Acrylic Tape (discontinued **)
Copyright © lookpolymers.com All Rights Reserved