Kennametal Stellite Stellite® 6 PM with P/M Processing

Category Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer Kennametal Stellite
Trade Name Stellite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kennametal Stellite Stellite® 6 PM with P/M Processing.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Data provide by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
Physical Properties Metric English Comments
Density 8.20 g/cc
0.296 lb/in³
P/M (98%)
8.38 g/cc
0.303 lb/in³
theoretical
Mechanical Properties Metric English Comments
Hardness, Brinell 364
364
Converted from Rockwell C hardness.
207

@Temperature 760 °C
 207

@Temperature 1400 °F
 Converted from Rockwell C hardness
284

@Temperature 649 °C
 284

@Temperature 1200 °F
 Converted from Rockwell C hardness
337

@Temperature 538 °C
 337

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Knoop 436
436
Converted from Rockwell C hardness.
241

@Temperature 760 °C
 241

@Temperature 1400 °F
 Converted from Rockwell C hardness
337

@Temperature 649 °C
 337

@Temperature 1200 °F
 Converted from Rockwell C hardness
402

@Temperature 538 °C
 402

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Rockwell A 70
70
Converted from Rockwell C hardness.
58

@Temperature 760 °C
 58

@Temperature 1400 °F
 Converted from Rockwell C hardness
65

@Temperature 649 °C
 65

@Temperature 1200 °F
 Converted from Rockwell C hardness
69

@Temperature 538 °C
 69

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Rockwell C 40
40
15

@Temperature 760 °C
 15

@Temperature 1400 °F
30

@Temperature 649 °C
 30

@Temperature 1200 °F
37

@Temperature 538 °C
 37

@Temperature 1000 °F
Hardness, Vickers 383
383
Converted from Rockwell C hardness.
212

@Temperature 760 °C
 212

@Temperature 1400 °F
 Converted from Rockwell C hardness
294

@Temperature 649 °C
 294

@Temperature 1200 °F
 Converted from Rockwell C hardness
352

@Temperature 538 °C
 352

@Temperature 1000 °F
 Converted from Rockwell C hardness
Tensile Strength, Ultimate 897 MPa
130000 psi
518 MPa

@Temperature 760 °C
 75100 psi

@Temperature 1400 °F
766 MPa

@Temperature 649 °C
 111000 psi

@Temperature 1200 °F
828 MPa

@Temperature 538 °C
 120000 psi

@Temperature 1000 °F
Elongation at Break <= 1.0 %
<= 1.0 %
in 25.4 mm
1.0 %

@Temperature 538 °C
 1.0 %

@Temperature 1000 °F
 in 25.4 mm
1.0 %

@Temperature 649 °C
 1.0 %

@Temperature 1200 °F
 in 25.4 mm
10 %

@Temperature 760 °C
 10 %

@Temperature 1400 °F
 in 25.4 mm
Thermal Properties Metric English Comments
CTE, linear 13.9 µm/m-°C

@Temperature 0.000 - 100 °C
 7.72 µin/in-°F

@Temperature 32.0 - 212 °F
14.1 µm/m-°C

@Temperature 0.000 - 200 °C
 7.83 µin/in-°F

@Temperature 32.0 - 392 °F
14.5 µm/m-°C

@Temperature 0.000 - 300 °C
 8.06 µin/in-°F

@Temperature 32.0 - 572 °F
14.7 µm/m-°C

@Temperature 0.000 - 400 °C
 8.17 µin/in-°F

@Temperature 32.0 - 752 °F
15.0 µm/m-°C

@Temperature 0.000 - 500 °C
 8.33 µin/in-°F

@Temperature 32.0 - 932 °F
15.3 µm/m-°C

@Temperature 0.000 - 600 °C
 8.50 µin/in-°F

@Temperature 32.0 - 1110 °F
15.8 µm/m-°C

@Temperature 0.000 - 700 °C
 8.78 µin/in-°F

@Temperature 32.0 - 1290 °F
16.3 µm/m-°C

@Temperature 0.000 - 800 °C
 9.06 µin/in-°F

@Temperature 32.0 - 1470 °F
16.9 µm/m-°C

@Temperature 0.000 - 900 °C
 9.39 µin/in-°F

@Temperature 32.0 - 1650 °F
17.4 µm/m-°C

@Temperature 0.000 - 1000 °C
 9.67 µin/in-°F

@Temperature 32.0 - 1830 °F
Melting Point 1260 - 1357 °C
2300 - 2475 °F
Solidus 1260 °C
2300 °F
Liquidus 1357 °C
2475 °F
Component Elements Properties Metric English Comments
Boron, B <= 1.0 %
<= 1.0 %
Carbon, C 1.2 %
1.2 %
Chromium, Cr 29 %
29 %
Cobalt, Co 52.3 %
52.3 %
As remainder
Iron, Fe <= 3.0 %
<= 3.0 %
Manganese, Mn 1.0 %
1.0 %
Molybdenum, Mo <= 1.5 %
<= 1.5 %
Nickel, Ni <= 3.0 %
<= 3.0 %
Other <= 2.0 %
<= 2.0 %
Silicon, Si <= 1.5 %
<= 1.5 %
Tungsten, W 4.5 %
4.5 %
Electrical Properties Metric English Comments
Magnetic Permeability <= 1.20

@Temperature 22.0 °C
 <= 1.20

@Temperature 71.6 °F
 200 Oersted