SABIC Innovative Plastics LNP THERMOCOMP UCF22S PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UCF22S PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* UCF22S is a compound based on Polyphthalamide resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Heat Stabilized, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.340 % | 0.340 % | 50% RH, 24 hrs; ASTM D570 |
| 0.560 % | 0.560 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 178 MPa | 25800 psi | 5 mm/min; ISO 527 |
| 188 MPa | 27300 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.76 GPa | 1851 ksi | 1 mm/min; ISO 527 |
| 12.98 GPa | 1883 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 249 MPa | 36100 psi | ISO 178 |
| 264 MPa | 38300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 10.43 GPa | 1513 ksi | 2 mm/min; ISO 178 |
| 10.8 GPa | 1570 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.520 J/cm | 0.974 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.21 J/cm | 7.89 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 47.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 74.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 275 °C | 527 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 280 °C @Thickness 3.20 mm |
536 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 262 °C @Thickness 3.20 mm |
504 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JLK51L Polyvinyl Chloride, Flexible (PVC, Flexible)
- 3M Dyneon™ TF 4220 PTFE 2% Cond. Pigm. Filled (discontinued **)
- ICE Hot Pressed SiC
- SABIC Innovative Plastics ULTEM 2210R PEI (Asia Pacific)
- Solvay Specialty Polymers Cogegum® GFR/340-HP Polyolefin
- Samsung Cheil Industries Infino® LS-1150G PC/ABS, 15% Glass Filled FR
- Samsung Cheil Industries Starex® MG-0330 ABS, Unreinforced Heat Resistant
- Trelleborg B870 Nitrile Rubber
- Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade
- Gwent Electronic Materials C2010309P3 Platinum Paste
Copyright © lookpolymers.com All Rights Reserved