Victrex® PEEK 150GL20 Polyetheretherketone, 20% Glass Fibre Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer Victrex
Trade Name PEEK
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 150GL20 Polyetheretherketone, 20% Glass Fibre Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description:High performance thermoplastic material, 20% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food contact compliant, colour natural/beige.Typical Application Areas:Complex geometries with thin cross sections or long flow lengths where good strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
Crystalline; ISO 1183
Water Absorption 0.050 %

@Temperature 23.0 °C,
Time 86400 sec
 0.050 %

@Temperature 73.4 °F,
Time 24.0 hour
 3.2mm thick tensile bar; ISO 62-1
Water Absorption at Saturation 0.40 %

@Temperature 23.0 °C
 0.40 %

@Temperature 73.4 °F
 Equilibrium; by immersion; ISO 62-1
0.45 %

@Temperature 100 °C
 0.45 %

@Temperature 212 °F
 Immersion; ISO 62-1
Viscosity 230000 cP

@Temperature 400 °C
 230000 cP

@Temperature 752 °F
 melt; ISO 11443
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
380°C nozzle, 180°C tool; ISO 294-4
Spiral Flow 16.0 cm

@Thickness 1.00 mm
 6.30 in

@Thickness 0.0394 in
 380°C nozzle, 180°C tool
Mechanical Properties Metric English Comments
Hardness, Shore D 86
86
ISO 868
Tensile Strength at Break 40.0 MPa

@Temperature 275 °C
 5800 psi

@Temperature 527 °F
 ISO 527
50.0 MPa

@Temperature 225 °C
 7250 psi

@Temperature 437 °F
 ISO 527
70.0 MPa

@Temperature 175 °C
 10200 psi

@Temperature 347 °F
 ISO 527
115 MPa

@Temperature 125 °C
 16700 psi

@Temperature 257 °F
 ISO 527
160 MPa

@Temperature 23.0 °C
 23200 psi

@Temperature 73.4 °F
 ISO 527
170 MPa

@Temperature -55.0 °C
 24700 psi

@Temperature -67.0 °F
 ISO 527
Elongation at Break 2.4 %

@Temperature 23.0 °C
 2.4 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 9.00 GPa

@Temperature 23.0 °C
 1310 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Strength 60.0 MPa

@Temperature 275 °C
 8700 psi

@Temperature 527 °F
 ISO 178
100 MPa

@Temperature 175 °C
 14500 psi

@Temperature 347 °F
 ISO 178
190 MPa

@Temperature 125 °C
 27600 psi

@Temperature 257 °F
 ISO 178
250 MPa

@Temperature 23.0 °C
 36300 psi

@Temperature 73.4 °F
 ISO 178
270 MPa

@Temperature -55.0 °C
 39200 psi

@Temperature -67.0 °F
 ISO 178
Flexural Modulus 8.50 GPa

@Temperature 23.0 °C
 1230 ksi

@Temperature 73.4 °F
 ISO 178
Izod Impact, Notched (ISO) 0.750 kJ/m²

@Temperature 23.0 °C
 0.357 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
Izod Impact, Unnotched (ISO) 3.50 kJ/m²

@Temperature 23.0 °C
 1.67 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/U
Charpy Impact Unnotched 3.50 J/cm²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1U
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 45.0 µm/m-°C

@Temperature <=143 °C
 25.0 µin/in-°F

@Temperature <=289 °F
 Average below Tg; ISO 11359
130 µm/m-°C

@Temperature >=143 °C
 72.2 µin/in-°F

@Temperature >=289 °F
 Average above Tg; ISO 11359
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature <=143 °C
 13.9 µin/in-°F

@Temperature <=289 °F
 Below Tg; ISO 11359
25.0 µm/m-°C

@Temperature >=143 °C
 13.9 µin/in-°F

@Temperature >=289 °F
 Above Tg; ISO 11359
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
Average; ISO 22007-4
0.350 W/m-K

@Temperature 23.0 °C
 2.43 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
 Along flow; ISO/CD 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 323 °C
613 °F
ISO 75-f
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
147 °C
297 °F
Midpoint; ISO 11357
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Dielectric Constant 3.2

@Frequency 1000 Hz,
Temperature 23.0 °C
 3.2

@Frequency 1000 Hz,
Temperature 73.4 °F
 IEC 60250
Dielectric Strength 23.0 kV/mm

@Thickness 2.50 mm
 584 kV/in

@Thickness 0.0984 in
 IEC 60243-1
Dissipation Factor 0.0040

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.0040

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
Comparative Tracking Index 150 V
150 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 380 °C
716 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 °C

@Time 18000 sec
 248 °F

@Time 5.00 hour
150 °C

@Time 10800 sec
 302 °F

@Time 3.00 hour