3A Composites Core Materials AIREX® C70.40 Universal Structural Foam

Category Other Engineering Material , Composite Core Material , Polymer
Manufacturer 3A Composites Core Materials
Trade Name AIREX®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3A Composites Core Materials AIREX® C70.40 Universal Structural Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AIREX® C70 is a closed cell, crosslinked polymer foam that combines excellent stiffness and strength to weight ratios with superior toughness. It is non-friable, contains no CFC’s, has negligible water absorption, and provides an excellent resistance to chemicals. A fine cell structure offers an excellent bonding surface. Compatible with most resins and manufacturing processes AIREX® C70 is ideally suited as a core material for a wide variety of lightweight sandwich structures subjected to both static and dynamic loads.Characteristicsoutstanding strength and stiffness to weight ratiosGood impact strengthLow resin absorptionHigh fatigue resistanceGood fire performance (self-extinguishing)Sound and thermal insulationGood styrene resistanceApplicationsMarine: Hulls, decks, bulkheads, superstructures, interiorsRoad and Rail: Roof panels, interiors, floors, doors, partition walls, side skirts, front-endsAircraft: Interiors, radomes, galley carts, general aviation (fuselage and wing)Recreation: Skis, snowboards, surfboards, wakeboards, canoes, kayaksIndustrial: Tooling, tanks, ductwork, containers, covers
Physical Properties Metric English Comments
Density 0.0400 g/cc
0.00145 lb/in³
average; ISO 845
Mechanical Properties Metric English Comments
Tensile Strength 0.700 MPa
102 psi
average; in the plane; ISO 527 1-2
Elongation at Break 8.0 %
8.0 %
average; shear; ISO 1922
Tensile Modulus 0.0280 GPa
4.06 ksi
average; in the plane; ISO 527 1-2
Compressive Strength 0.450 MPa
65.3 psi
perpendicular to plane; ISO 844
Compressive Modulus 0.0410 GPa
5.95 ksi
average; perpendicular to plane; DIN 53421
Shear Modulus 0.0130 GPa
1.89 ksi
average; ASTM C393
Shear Strength 0.450 MPa
65.3 psi
average; ISO 1922
Thermal Properties Metric English Comments
Thermal Conductivity 0.0310 W/m-K
0.215 BTU-in/hr-ft²-°F
ISO 8301
Descriptive Properties Value Comments
Color light green