SABIC Innovative Plastics LNP THERMOCOMP SH0430AC_BK1D466 PA12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP SH0430AC_BK1D466 PA12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
4.3 specific gravity nylon 12, clean compound system
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.27 g/cc | 0.154 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0081 - 0.0101 cm/cm @Time 86400 sec |
0.0081 - 0.0101 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0087 - 0.0107 cm/cm @Time 86400 sec |
0.0087 - 0.0107 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
| 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
| 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 3.2 % | 3.2 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.72 GPa | 685 ksi | 1 mm/min; ISO 527 |
| 4.80 GPa | 696 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 69.0 MPa | 10000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.25 GPa | 616 ksi | 2 mm/min; ISO 178 |
| 4.32 GPa | 627 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.660 J/cm | 1.24 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.81 J/cm | 9.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.5 - 75.5 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.8 - 41.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | >= 66.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
>= 37.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 101 °C @Thickness 3.20 mm |
214 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products FRP257-01 32% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Black
- NatureWorks® Ingeo™ AW 240D Biopolymer for Food Serviceware
- Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes
- Shakespeare ISOray Fluoropolymer UV resistant sewing thread, diameter 0.006"
- Solvay Specialty Polymers Hyflon® PFA P450 Perfluoroalkoxy (PFA)
- Solvay GEROPON® CYA/75 Surfactant
- Saint-Gobain COHRlastic® 500 General Purpose Silicone Solid Rubber
- CP-Polymer-Technik Wellamid® 6000/42 Nylon 6, Polymer Modified, Dry
- 3M 9499 Splicing Tapes
Copyright © lookpolymers.com All Rights Reserved