SABIC Innovative Plastics LNP THERMOCOMP RX04515H PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP RX04515H PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* RX04515H is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Physical Properties Metric English Comments
Specific Gravity 1.33 g/cc
1.33 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Time 86400 sec
 0.0040 - 0.0060 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 278 MPa
40300 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 1.6 %
1.6 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 30.8 GPa
4470 ksi
5 mm/min; ASTM D638
Flexural Strength 413 MPa
59900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 23.7 GPa
3440 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 1.01 J/cm
1.89 ft-lb/in
ASTM D256
Izod Impact, Unnotched 9.71 J/cm
18.2 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 255 °C

@Thickness 3.20 mm
 491 °F

@Thickness 0.126 in
 unannealed; ASTM D648