SABIC Innovative Plastics LNP THERMOCOMP RF003ES PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF003ES PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF003ES is a Nylon 66 base resin containing 15% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 | |
| Moisture Absorption | 1.10 % | 1.10 % | 50% RH, 24 hrs; ASTM D570 |
| 1.60 % | 1.60 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Time 86400 sec |
0.0070 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
| 115 MPa | 16700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
| 115 MPa | 16700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 |
| 3.2 % | 3.2 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 |
| 3.2 % | 3.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.94 GPa | 862 ksi | 50 mm/min; ASTM D638 |
| 5.96 GPa | 864 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 128 MPa | 18600 psi | ISO 178 |
| 174 MPa | 25200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 174 MPa | 25200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | 2 mm/min; ISO 178 |
| 4.74 GPa | 687 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.89 J/cm | 9.16 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J @Temperature 23.0 °C |
1.48 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 82.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
45.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Niche Polymer PA66MIN Nylon 66, Medium Impact
- Parker Chomerics Tecknit Consil®-A 897 Silver-Aluminum Filled Silicone Elastomer
- MV Labs NH400 NH4Cl Ammonium chloride
- Spartech Polycast SP 1.25 Cell Cast Acrylic
- Teknor Apex Telcar® OBC 2419A Thermoplastic Elastomer
- Elastocon TPE Technologies Elastocon® 8138B Thermoplastic Elastomer
- Arlon 56581R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- ConocoPhillips Conoco® El Mar® Ashless Supreme Oil, SAE Viscosity Grade 30
- Overview of materials for Polypropylene with Glass Fiber + PTFE
Copyright © lookpolymers.com All Rights Reserved