SABIC Innovative Plastics LNP THERMOCOMP RC004SXS PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RC004SXS PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RC004SXS is a compound based on Nylon 66 containing 20% Carbon Fiber. Added feature of this grade includes: Heat Stabilized, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.890 % | 0.890 % | 50% RH, 24 hrs; ASTM D570 |
| 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 222 MPa | 32200 psi | Type I, 5 mm/min; ASTM D638 |
| 242 MPa | 35100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| 2.5 % | 2.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 16.68 GPa | 2419 ksi | 50 mm/min; ASTM D638 |
| 16.74 GPa | 2428 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 331 MPa | 48000 psi | ISO 178 |
| 348 MPa | 50500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 12.92 GPa | 1874 ksi | 2 mm/min; ISO 178 |
| 13.7 GPa | 1990 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.670 J/cm | 1.26 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.84 J/cm | 16.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 89.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
49.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 868H (FG) Synthetic Oil
- Okulen® 2000 PE-UHMW, F-Ex
- Polykemi AB POLYshine PBT D401 R PBT, Medium Viscosity
- Nilit FRIANYL B63 MG30 Nylon 6 for injection molding, 30% mineral filled
- DSM Somos® 9120 Epoxy Photopolymer (Unverified Data**)
- Ipiranga Petrochem GM 8250 HDPE
- Samsung Cheil Industries Starex® TX-0520 TRABS, Unreinforced
- Fainplast Compounds CR 0118 Flexible PVC, Electrical Bedding
- Sumitomo Bakelite North America RX® 865M Novolac Phenolic
Copyright © lookpolymers.com All Rights Reserved