Spartech EP6430 Filled and Reinforced Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer Spartech
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Spartech EP6430 Filled and Reinforced Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Filled copolymers offer a higher level of impact performance than homopolymer materials, and higher stiffness than unfilled copolymers. Copolymer based materials retain much of their impact strength at low temperatures. Typical applications include thermoformed frozen food containers, extruded and blow molded automotive and construction materials, and blow molded recreational equipment.Information provided by Spartech
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc

@Temperature 22.8 °C
1.12 g/cc

@Temperature 73.0 °F
ASTM D792
Filler Content 30 %
30 %
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
0.125inch wall
Mechanical Properties Metric English Comments
Tensile Strength, Yield 68.9 MPa
10000 psi
ASTM D638
Elongation at Break 4.0 %
4.0 %
ASTM D638
Elongation at Yield 4.0 %
4.0 %
ASTM D638
Flexural Modulus 4.14 GPa
600 ksi
secant; ASTM D790
5.86 GPa
850 ksi
tangent; ASTM D790
Izod Impact, Notched 2.14 J/cm

@Temperature 22.8 °C
4.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 2.71 J

@Temperature -5.56 °C
2.00 ft-lb

@Temperature 22.0 °F
ASTM D5420
13.6 J

@Temperature 22.8 °C
10.0 ft-lb

@Temperature 73.0 °F
ASTM D5420
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 157 °C
315 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 132 °C
270 °F
ASTM D648
Optical Properties Metric English Comments
Gloss <= 50 %
<= 50 %
60°; ASTM D523