SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* QF008 is a compound based on Nylon 6/10 resin containing 40% Glass Fiber.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ASTM D792
1.42 g/cc
0.0513 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 171 MPa
24800 psi
ASTM D638
183 MPa
26500 psi
ISO 527
Elongation at Break 3.3 %
3.3 %
ASTM D638
Tensile Modulus 12.42 GPa
1801 ksi
50 mm/min; ASTM D638
Flexural Strength 255 MPa
37000 psi
ASTM D790
Flexural Modulus 10.78 GPa
1564 ksi
ISO 178
10.79 GPa
1565 ksi
ASTM D790
Izod Impact, Notched 1.38 J/cm
2.59 ft-lb/in
ASTM D256
Izod Impact, Unnotched 11.21 J/cm
21.00 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 219 °C

@Thickness 3.20 mm
 426 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 214 °C
417 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
207 °C

@Thickness 3.20 mm
 405 °F

@Thickness 0.126 in
 unannealed; ASTM D648