Arkema Group Solarkote® P-611 Acrylic

Category	Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded
Manufacturer	Arkema
Trade Name	SolarKote®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Solarkote® P-611 Acrylic.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

PVC capstock, white, low glossInformation provided by Arkema Group

Physical Properties	Metric	English	Comments
Specific Gravity	1.16 g/cc	1.16 g/cc	ASTM D792
Water Absorption	0.40 %	0.40 %	weight gain after 24 hr. immersion; ASTM D570
Melt Flow	0.50 g/10 min @Load 3.80 kg, Temperature 230 °C	0.50 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	69	69	ASTM D785
Tensile Strength, Ultimate	19.3 MPa	2800 psi	ASTM D638
Elongation at Break	85 %	85 %	ASTM D638
Tensile Modulus	1.21 GPa	176 ksi	ASTM D638
Flexural Strength	<= 33.1 MPa	<= 4800 psi	ASTM D790
Flexural Modulus	1.17 GPa	170 ksi	ASTM D790
Izod Impact, Notched	0.961 J/cm	1.80 ft-lb/in	ASTM D256
Taber Abrasion, mg/1000 Cycles	16.5	16.5	500 g load; ASTM D1044

Thermal Properties	Metric	English	Comments
CTE, linear	117 µm/m-°C @Temperature -17.8 °C	65.0 µin/in-°F @Temperature 0.000 °F	ASTM E831
	124 µm/m-°C @Temperature -6.67 °C	69.0 µin/in-°F @Temperature 20.0 °F	ASTM E831
	137 µm/m-°C @Temperature 23.9 °C	76.0 µin/in-°F @Temperature 75.0 °F	ASTM E831
	149 µm/m-°C @Temperature 37.8 °C	83.0 µin/in-°F @Temperature 100 °F	ASTM E831
Thermal Conductivity	0.216 W/m-K	1.50 BTU-in/hr-ft²-°F	ASTM C177
Deflection Temperature at 1.8 MPa (264 psi)	51.7 °C	125 °F	annealed; ASTM D648
Vicat Softening Point	58.3 °C	137 °F	50°C/hr; 50N; ASTM D1525
	68.9 °C	156 °F	50°C/hr; 10N; ASTM D1525