3M 5200 Marine Adhesive/Sealant

Category Polymer , Adhesive
Manufacturer 3M
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M 5200 Marine Adhesive/Sealant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Marine Adhesive/Sealant 5200 is a one-part polyurethane that chemically reacts with moisture to deliver strong, flexible bonds. It has excellent adhesion to wood, gelcoat and fiberglass. It forms a watertight, weather-resistant seal on joints and boat hardware, above and below the waterline. In addition, its flexibility allows for dissipation of stress caused by shock, vibration, swelling or shrinkingFeatures:Tough/flexible polyurethane polymer Non-shrinking One-part moisture cure Long working timeInformation provided by 3M
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
Solids Content 97 %
97 %
Mechanical Properties Metric English Comments
Hardness, Shore A 68
68
cured
Tensile Strength at Break 4.37 MPa
634 psi
Salt Water
4.37 MPa

@Time 4.493e+6 sec
634 psi

@Time 1248 hour
Fresh Water
4.86 MPa

@Time 4.493e+6 sec
705 psi

@Time 1248 hour
50% RH
Elongation at Break 802 %
802 %
Salt Water
762 %

@Time 4.493e+6 sec
762 %

@Time 1248 hour
50% RH
805 %

@Time 4.493e+6 sec
805 %

@Time 1248 hour
Fresh Water
Shear Strength 0.331 MPa
48.0 psi
Overlap, Polyethylene, 50% RH
0.379 MPa
55.0 psi
Overlap, Polypropylene, 50% RH
0.738 MPa
107 psi
Overlap, Lead, 50% RH
1.21 MPa
175 psi
Overlap, Nylon, 50% RH
1.37 MPa
198 psi
Overlap, Copper, 50% RH
1.50 MPa
217 psi
Overlap, Acrylic, 50% RH
1.59 MPa
231 psi
Overlap, ABS, 50% RH
1.74 MPa
252 psi
Overlap, Bronz, 50% RH
2.43 MPa
352 psi
Overlap, Stainless Steel, 50% RH
2.50 MPa
362 psi
Overlap, Fiberglass, 50% RH
2.63 MPa
381 psi
Overlap, Polycarbonate, 50% RH
2.71 MPa
393 psi
Overlap, Aluminum, 50% RH
3.27 MPa
474 psi
Overlap, Brass, 50% RH
3.34 MPa
484 psi
Overlap, Zinc (Galvanized), 50% RH
3.46 MPa
502 psi
Overlap, Teak, 50% RH
3.58 MPa
519 psi
Overlap, Gelcoat, 50% RH
3.71 MPa
538 psi
Overlap, Steel, 50% RH
3.79 MPa
549 psi
Overlap, Oak, 50% RH
3.89 MPa
564 psi
Overlap, Mahogany, 50% RH
4.52 MPa
656 psi
Overlap, Maple, 50% RH
4.69 MPa
680 psi
Overlap, Pine, 50% RH
4.83 MPa
700 psi
Overlap, Fir, 50% RH
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 88.0 °C
190 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Processing Properties Metric English Comments
Cure Time 240 min

@Temperature 32.0 °C
4.00 hour

@Temperature 89.6 °F
Open Time, 90% RH
1800 min

@Temperature 21.0 °C
30.0 hour

@Temperature 69.8 °F
Open Time, 50% RH
7200 min

@Temperature 21.0 °C
120 hour

@Temperature 69.8 °F
Full Cure, 50% RH
Shelf Life 24.0 Month

@Temperature 16.0 - 26.0 °C
24.0 Month

@Temperature 60.8 - 78.8 °F