SABIC Innovative Plastics LNP THERMOCOMP PH0320A PA 6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PH0320A PA 6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* PH0320A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.06 g/cc | 0.111 lb/in³ | ISO 1183 |
| 3.071 g/cc | 0.1109 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.360 % | 0.360 % | 50% RH, 24 hrs; ASTM D570 |
| 0.490 % | 0.490 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0108 cm/cm @Time 86400 sec |
0.0108 in/in @Time 24.0 hour |
ISO 294 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
| 61.0 MPa | 8850 psi | ASTM D638 | |
| Elongation at Break | 1.1 % | 1.1 % | ISO 527 |
| 1.4 % | 1.4 % | ASTM D638 | |
| Tensile Modulus | 5.80 GPa | 841 ksi | 1 mm/min; ISO 527 |
| 6.04 GPa | 876 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
| 95.0 MPa | 13800 psi | ISO 178 | |
| Flexural Modulus | 5.26 GPa | 763 ksi | ISO 178 |
| 5.28 GPa | 766 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.61 J/cm | 4.89 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 51.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 51.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 60.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 60.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8512F (842G0) (UF) Synthetic Oil
- Abatron 222 A/B Filled Potting Compound (discontinued **)
- Lucite International Diakon® ST50G8 Toughened Acrylic Polymer
- Techmer ES HiFill FR® ABS FR BK
- Techmer ES Statiblend® PA6/6 02013
- Cheng Yu Plastic PP222 Flame Retardant Polypropylene, High Impact
- Advanced Polymer Alloys Alcryn® 2070 BK Melt Processable Rubber
- Beijing Ranger Chem SM-607R Solid Epoxy Resin
- Vyncolit Neopreg Kinel® SK60 L8F Glass Fiber Reinforced Molding Compound
- Radici Radilon® A 38 (dry) Nylon 66
Copyright © lookpolymers.com All Rights Reserved