SABIC Innovative Plastics LNP THERMOCOMP PF00ASXS PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PF00ASXS PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* PF00ASXS is a compound based on Nylon 6 resin containing 50% Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.830 % | 0.830 % | 50% RH, 24 hrs; ASTM D570 |
| 0.970 % | 0.970 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0070 cm/cm @Time 86400 sec |
0.0060 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 213 MPa | 30900 psi | ASTM D638 |
| 241 MPa | 35000 psi | ISO 527 | |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| 3.0 % | 3.0 % | ISO 527 | |
| Tensile Modulus | 17.09 GPa | 2479 ksi | 50 mm/min; ASTM D638 |
| 17.25 GPa | 2502 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 318 MPa | 46100 psi | ISO 178 |
| 328 MPa | 47600 psi | ASTM D790 | |
| Flexural Modulus | 12.29 GPa | 1783 ksi | ASTM D790 |
| 12.38 GPa | 1796 ksi | ISO 178 | |
| Izod Impact, Notched | 1.76 J/cm | 3.30 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 94.0 kJ/m² | 44.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 18.0 J | 13.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 22.0 J | 16.2 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 198 °C @Thickness 3.20 mm |
388 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs HO700 Ho(NO3)3·5H2O Holmium nitrate pentahydrate
- LG Chemical LUPOY GP-2401F General Purpose Modified PC, 40% Glass Fiber Reinforced, Flame Retardant
- H.C. Starck HPM 1850 Tungsten High Density Composite
- Techmer ES HiFill FR® HIPS FR V-2
- Struktol POLYDIS 3680 Elastomer modified epoxy prepolymer
- A. Schulman SCHULAFLEX® SF 230 Ethylene-Based Butene Plastomer
- Eurostar Starpylen MFB44S PP, Glass Bead/Glass Fiber Filled
- Chesterton 706 FG Rustsalvo®
- Polyram RamTough PZ715 Polycarbonate, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved