SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM4025 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM4025 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* Noryl_HM4025 compound is a 40% Glass/Mineral filled high modulus grade. DTUL 255F (124C). UL94 V-0/V-1/5VA rated in black and gray only (see thicknesses).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Thickness 3.20 mm |
0.0015 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 158 MPa | 22900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Poissons Ratio | 0.38 | 0.38 | ASTM E 132 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Static | 0.42 | 0.42 | steel; ASTM D1894 |
| 0.44 | 0.44 | self; ASTM D1894 | |
| Taber Abrasion, mg/1000 Cycles | 35 | 35 | CS-17, 1 kg; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.6 µm/m-°C @Temperature -40.0 - 95.0 °C |
12.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 32.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
18.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.47 mm |
V-1 @Thickness 0.0579 in |
UL 94 |
| V-0 @Thickness 2.99 mm |
V-0 @Thickness 0.118 in |
UL 94 | |
| 5VA @Thickness 2.51 mm |
5VA @Thickness 0.0988 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in air; ASTM D149 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Ovation Polymers RIGITRON 10001 Polycarbonate
- Precision Polymer Engineering C60M Chloroprene Rubber
- LG Chemical SEETEC EF221 Ethylene Vinyl Acetate
- Lucite International Elvacite ® 3009 Acrylic Resin
- Solvay Chemicals Oxyper® SHC Sodium Percarbonate
- Tra-Con Tra-Bond FDA2T Food and Drug Application Epoxy Adhesive
- Addiplast Addilene PMD 50213 Polypropylene Copolymer
- EMS-Grivory Grivory® GVX-5 H black 9915 PA*-GF50
- Buckeye Polymers BP PPC 0218-22 BLK Polypropylene Copolymer
- Compuestos Dominicanos Polycom AU-050695 PVC Compound
Copyright © lookpolymers.com All Rights Reserved