SABIC Innovative Plastics LNP THERMOCOMP MH0500C PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MH0500C PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* MH0500C is a compound based on Polypropylene resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 5.03 g/cc | 0.182 lb/in³ | ISO 1183 |
| 5.04 g/cc | 0.182 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.015 - 0.017 cm/cm @Time 86400 sec |
0.015 - 0.017 in/in @Time 24.0 hour |
ASTM D955 |
| 0.016 cm/cm @Time 86400 sec |
0.016 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ISO 294 |
| 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| 19.0 MPa | 2760 psi | ISO 527 | |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| 19.0 MPa | 2760 psi | ISO 527 | |
| Elongation at Break | 13.6 % | 13.6 % | ISO 527 |
| 19.5 % | 19.5 % | ASTM D638 | |
| Elongation at Yield | 3.2 % | 3.2 % | ASTM D638 |
| 3.3 % | 3.3 % | ISO 527 | |
| Tensile Modulus | 2.92 GPa | 424 ksi | 1 mm/min; ISO 527 |
| 4.13 GPa | 599 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 31.0 MPa | 4500 psi | ISO 178 |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D790 |
| 2.90 GPa | 421 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 61.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 80.0 °C @Thickness 3.20 mm |
176 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Petromont 1202 High Density Polyethylene Resin
- Northstar Polymers MPG-A25A Room-Temperature Curable Liquid Castable Polyurethane
- MetalTek MTEK N-12MV Cast UNS N30012 Severe Corrosion and Heat Resistant Alloy
- SABIC Innovative Plastics LNP Lubricomp EL004 PEI (Asia Pacific)
- Techmer ES Luriblend® POM CO GF10 TX15 BK 10% Glass Filled
- CMW® ELKONIUM 73 Copper Cadmium Alloy with Au/Ag-Cladding
- Zircar Refractory Composites ASPA-1 Alumina-Silica Fiber Paper
Copyright © lookpolymers.com All Rights Reserved