PolyOne Edgetek® COC BLEND-15GF Natural Cyclic Olefin Copolymer (COC)
| Category | Polymer , Thermoplastic , Cyclo Olefin Polymer |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® COC BLEND-15GF Natural Cyclic Olefin Copolymer (COC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.8 MPa | 11000 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 5.49 GPa | 796 ksi | 5.1 mm/min; ASTM D638 |
| Flexural Strength | 121 MPa | 17500 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 5.17 GPa | 750 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.806 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | Unannealed; ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Glass Fiber Reinforcement | |
| Forms | Pellets | |
| Generic Material | COC | |
| Generic Name | Cyclic Olefin Copolymer (COC) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- Nye Lubricants 380 (RL) Synthetic Oil
- LG Chemical LUPOY GN2201FM PC+GF20%, Halogen Free, Flame Retardant, Heat Resistance
- MRC Polymers NAXALOYâ„¢ 793MF6 PC + Polyester Blend, 6% Mineral Filled
- Styrolution Novodur® 250 ABS
- SABIC Innovative Plastics LNP STAT-KON DX02437 PC (Asia Pacific)
- TIMET TIMETAL® 6-2-4-6 Titanium Alloy (Ti-6Al-2Sn-4Zr-6Mo), 10% Equiaxed Alpha + Annealed
- ExxonMobil LLDPE LL 3201.69 Linear Low Density Polyethylene Resin
- Entec Hylex® P1310FR Polycarbonate
- Chosun Refractories SAL90CR Special High Alumina brick
- Denka VINYKON R3102 PVC, R grade for hard extrusion
Copyright © lookpolymers.com All Rights Reserved